Trial Purpose:

The purpose of this experiment was to determine the effectiveness of Liquinox in removing the white buffing compound from stainless steel coupons via heated immersion with a stir bar.

Date Run:

07/16/2020

Experiment Procedure:

Three stainless steel coupons were obtained and weighed. The white buffing compound soil was applied to the bottom third of the coupons with a swab and a soiled weight was recorded. Coupons were then submerged into a 1% concentration solution of Liquinox at 170°F for five minutes. When the five minutes passed, coupons were air dried, and a clean weight was recorded. Effectiveness of the cleaner was determined.

Trial Results:

Cleaner Initial wt. of cont. Final wt. of cont. % Cont. Removed %AVG
Liquinox 0.0049 -0.0009 118.37 151.92
0.0034 -0.002 158.82
0.0014 -0.0011 178.57

Success Rating:

Results successful using TACT (time, agitation, concentration, and temperature, as well as rinsing and drying) and/or other cleaning chemistries examined.

Conclusion:

The Liquinox at a 1% concentration and temperature of 170°F with a stir bar for agitation was effective in removing the white buffing compound from stainless steel coupons. Soil was removed at an average of 151.92%. Percent removals of over 100% indicate that excess soil from previous experiments was also removed from the coupons.